Stainless steel alloys with the term PH in their name indicate that they are precipitation hardened alloys. Typically a precipitation hardening or PH stainless steel alloy such as 15-5 Ph Rod is known to have high resistance to corrosion. It is not unusual for PH alloys to be heat treated in order to increase the tensile strengths of these alloys between the range of 850 MPa to 1700 MPa and yield strengths of 520 MPA to more than 1500 MPa.
In the case of the UNS S15500 Square And Cold Finished Bar, different heat treatments will yield different tensile strengths. However, the tensile strength values for each heat treatment carried out on the alloy would result in the AMS 5659 15-5PH Bright/ Flat Bar exhibiting tensile strength as high as in the range of 792 MPa - 1310 MPa. Since PH alloy exhibits properties such as high strength, corrosion resistance, the DIN 1.4545 Hex Bars are used in industries such as oil and gas, nuclear, and aerospace industries.
The name of this alloy is a derivative of the type of alloy it is as well as the content of 15% Chromium and 5% Nickel added in the 15-5ph Stainless Steel Round Bar. Another benefit of using the alloy is that it is readily weldable and it is possible to machine the 15-5 PH Round Bar, using any heat conditions suited to this grade including the following treatments H900, H925, H1025, H1075, H1100, H1150, Double H1150 & H1150M .
Dimensions | DIN, EN, ASTM, JIS, ASME, BS, AISI |
---|---|
Round bar size | Diameter: 3-~800mm |
Flat bar size | Thickness: 2 -100mm |
Width: 10 to 500mm | |
Angle bar size | 3mm*20mm*20mm~12mm*100mm*100mm |
Channel Bar | 80 x 40mm to 150 x 75mm section; 5.0 to 6.0mm thickness |
Rectangular Bars Section | 3.0 to 12.0mm thickness |
Billet Size | 1/2 to 495mm Diameter |
Rectangles Size | 33 x 30mm to 295 x 1066mm |
Hollow Bar | 32mm OD x 16mm ID to 250mm OD x 200mm ID) |
Dimensions | Diameter / Height: |
Tolerance | H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements |
Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
Surface | Hot Rolled Pickled, Bright, Sand Blasting Finished, Cold Drawn, Hairline,Polished |
Condition | Hardened & tempered, annealed |
Technique | Stainless Steel Cold Drawn, Hot Rolled, Forged Round Bar,Cold Rolled, Rod |
Processing | Bar cutting to 650mm |
Form | Rod, Round, Channel Bar, T-Bar, Flat Bar, Precision Ground Bar, Blocks, Square, Rings, Round Rod, Triangle, Hollow, Rectangle, Threaded, Hex (A/F), Profiles, Half Round Bar, Ingot, Billet, I/H Bar, Forging etc. |
Grade | C | P | Si | Ni | Al | Fe | Mn | S | Cr | Cb+Ta |
SS 15-5PH | 0.07 | 0.04 | 1.0 | 3.5 – 5.5 | – | Bal | 1.0 | 0.03 | 14.0 – 15.5 | 0.15 – 0.45 |
STANDARD | WERKSTOFF NR. | UNS |
SS 15-5PH | 1.4545 | S15500 |
Material | Condition |
Ultimate Tensile Strength (ksi) | 0.2 % Yield Strength (ksi) | Elongation % in 2D | % Reduction of Area | Rockwell C Hardness |
Alloy 15-5 PH Bar AMS 5659 |
Cond A | – | – | – | – | 363 HB max |
Alloy 15-5 PH Bar AMS 5659 |
H900 | 190 | 170 | 10 | 35 | 388-444 |
Alloy 15-5 PH Bar AMS 5659 |
H925 | 170 | 155 | 10 | 38 | 375-429 |
Alloy 15-5 PH Bar AMS 5659 |
H1025 | 155 | 145 | 12 | 45 | 331-401 |
Alloy 15-5 PH Bar AMS 5659 |
H1075 | 145 | 125 | 13 | 45 | 311-375 |
Alloy 15-5 PH Bar AMS 5659 |
H1100 | 140 | 115 | 14 | 45 | 302-363 |
Alloy 15-5 PH Bar AMS 5659 |
H1150 | 135 | 105 | 16 | 50 | 277-352 |