The use of stainless steel bars is prevalent in so many aspects of engineering. From being used in the general assembly to being used as manufacturing components, the SS 304 Square Bar, remains to date, one of the most economically feasible option. Amongst several stainless steel grades, alloy 304 offers moderate corrosion resistance properties, with moderately high strength. Since the alloying content of grade 304 8mm Stainless Steel Hollow Square Bar is 18% chromium with 8% nickel, the cost of the bar is lower in comparison to many molybdenum bearing alloys.
In applications that have the need for higher strength and higher corrosion resistance properties, the manufacturer may suggest using a SS 316 Square Bar, which is the next best alternative. Most of the orders received by any Stainless Steel Square Bar Manufacturer In India are for applications that include ornamentation or decorative purposes, railings, protective window barriers, or even gates.
What makes the Polished Stainless Steel Square Bar so perfect is that they could have a finish such that the bars have a reflective surface, which in the case of ornamentation purposes is considered to be ideal. The finishing could also include a mirror effect, which would depend on the end use requirement. Generally, Cold Finished Square Bar tends to have a better finish, and the component has edges that have superior definition in comparison to hot finished ones. Contrarily, the Hot Finished Square Bar makes use of heat, and so the processing time becomes shorter. Therefore the cost of processing becomes lower.
before buy Compare Stainless Steel Square Bar price with inconel 625 round bar price list
Square bars, otherwise called square steel, squares and square metal bar are a multipurpose steel area essentially utilized for assembling and fixes. Universally useful square bars are important for our light and re-moved segment, making it reasonable for regular business ventures.
Width X Depth |
Width X Depth |
Width X Depth |
MM |
MM |
MM |
4X4 |
19X19 |
45X45 |
5X5 |
20X20 |
48X48 |
6X6 |
21X21 |
50X50 |
7X7 |
22X22 |
53X53 |
8X8 |
24X24 |
56X56 |
9X9 |
25X25 |
60X60 |
10X10 |
26X26 |
63X63 |
11X11 |
28X28 |
67X67 |
12X12 |
30X30 |
70X70 |
13X13 |
32X32 |
75X75 |
14X14 |
34X34 |
80X80 |
15X15 |
35X35 |
85X85 |
16X16 |
38X38 |
90X90 |
17X17 |
40X40 |
95X95 |
18X18 |
42X42 |
100X100 |
| Description | Per Unit (INR) | Price in USD | Price in EURO |
|---|---|---|---|
| Eras-12 Friction Stay -18mm Square Groove, 2 Bar 2.5mm Thickness, With Plastic Slider. 100pcs/ctn Punch -made Of S.stee | 188 | 2.54 | 2.09 |
| 80cm Long Bar And Square Shower Head (Wt : 0.68 Kgs) (Showerhead ) (S.s ) | 104 | 1.41 | 1.16 |
| Ss 310s Square Bar 50/50 (Lg=1500mm) - 120700 - (Qty:2 Num Euro 389.1720 Per Num) | 155,560 | 2101.63 | 1729.00 |
| Stainless Steel Square Bar-410s | 401 | 5.42 | 4.46 |
| Sunrise Hydraulic Ironworkers Iw-60s Without Round/square Bar Shear Tool S/no 16030400 | 544,745 | 7359.56 | 6054.68 |
| Paddlewheel Aerator Sc-1.5 ( 2 Hp 380v 50 Hz Three Phase With Float Without Square Pipe S.s. Solid Shaft& Setting Bar | 17,346 | 234.35 | 192.80 |
| Paddlewheel Aerator Scd-1.5 ( 2 Hp 230v 50hz Single Phase With Float Without Square Pipe S.s Solid Shaft&setting Bar | 18,042 | 243.75 | 200.53 |
| Square Bar Steel 140., S235jr | 650 | 8.78 | 7.22 |
| Sunrise Hydraulic Ironworker Iw-50a S/l No 15120242without Round Square Bar Shearing Tool | 397,919 | 5375.93 | 4422.75 |
| Hot Rolled Square Bar Grade:s45c Size:20mm X 20mm X 4040mm (Alloy Steel) (Crt. No. 150227357276401910 Dt.24.11.2015) | 135 | 1.82 | 1.50 |
| Hot Rolled Square Bar Grade:s45c Size:20mm X 20mm X 4040mm (Alloy Steel) (Crt.no. 150294351276501410 Dt.24.11.2015) | 135 | 1.82 | 1.50 |
| Square Bar 14 L.40 For Crushing Machinesvb File No:s/9-37 Gatt/1997 Gvc Dt.13.02.2015 | 192 | 2.59 | 2.13 |
| Stainless Steel Bar - Square Bar, Xm19, Uns S20910 - 40 X 40 Mm | 751 | 10.15 | 8.35 |
| Stainless Steel Square Bar Size and Theoretical Weight | |||||||
| Size (mm) | Weight (kg/m) | Size (mm) | Weight (kg/m) | Size (mm) | Weight (kg/m) | Size (mm) | Weight (kg/m) |
| 3 × 3 | 0.071 | 15 × 15 | 1.784 | 30 × 30 | 7.137 | 60 × 60 | 28.548 |
| 4 × 4 | 0.127 | 16 × 16 | 2.03 | 32 × 32 | 8.12 | 63 × 63 | 31.474 |
| 5 × 5 | 0.198 | 17 × 17 | 2.292 | 34 × 34 | 9.167 | 67 × 67 | 35.598 |
| 6 × 6 | 0.285 | 18 × 18 | 2.569 | 35 × 35 | 9.714 | 70 × 70 | 38.857 |
| 7 × 7 | 0.389 | 19 × 19 | 2.863 | 38 × 38 | 11.451 | 75 × 75 | 44.606 |
| 8 × 8 | 0.508 | 20 × 20 | 3.172 | 40 × 40 | 12.688 | 80 × 80 | 50.752 |
| 9 × 9 | 0.642 | 21 × 21 | 3.497 | 42 × 42 | 13.989 | 85 × 85 | 52.294 |
| 10 × 10 | 0.793 | 22 × 22 | 3.838 | 45 × 45 | 16.058 | 90 × 90 | 64.233 |
| 11 × 11 | 0.96 | 24 × 24 | 4.568 | 48 × 48 | 18.271 | 95 × 95 | 71.568 |
| 12 × 12 | 1.142 | 25 × 25 | 4.956 | 50 × 50 | 19.825 | 100 × 100 | 79.3 |
| 13 × 13 | 1.34 | 26 × 26 | 5.361 | 53 × 53 | 22.275 | ||
| 14 × 14 | 1.554 | 28 × 28 | 6.217 | 56 × 56 | 24.868 | ||
| Siding × Siding × 0.00793 = Weight (kg) per meter | |||||||
the square bar is that strong steel bar made of steel ingots through squeezing, anyway the very unique square tube is empty segment with cycle of welding the pipe's billets.
| CD | Cold drawn | P | Polished |
| BD | Bright drawn | SRE | Slit rolled edge |
| CG | Centreless ground | HF | Hot finished |
| CF | Cold finished | HRAP | Hot rolled annealed and pickled |
| P&T | Peeled and turned | RT | Rough turned/peeled |
| ST | Smooth turned | PR | Peeled and reeled |
CF Tolerances |
Plus |
Minus |
1/8″ to 5/16″ (exclusive) |
0.000 |
0.002 |
5/16″ to 1/2″ (exclusive) |
0.000 |
0.003 |
1/2″ to 1″ (inclusive) |
0.000 |
0.004 |
over 1″ to 2″ (inclusive) |
0.000 |
0.006 |
over 2″ to 3″ (inclusive) |
0.000 |
0.008 |
Cold Finished Square Bar Straightness Tolerance:
CF: 1/16 inch in any 5 foot; but may not exceed 1/16 X (length in ft/5)
HF Tolerances |
Plus |
Minus |
Out of Sq |
Over 7/8″ to 1″ (inclusive) |
0.009 |
0.009 |
0.013 |
Over 1″ to 1-1/8″ (inclusive) |
0.010 |
0.010 |
0.015 |
Over 1-1/8″ to 1-1/4″ (inclusive) |
0.011 |
0.011 |
0.016 |
Over 1-1/4″ to 1-3/8″ (inclusive) |
0.012 |
0.012 |
0.018 |
Over 1-3/8″ to 1-1/2″ (inclusive) |
0.014 |
0.014 |
0.021 |
Over 1-1/2″ to 2″ (inclusive) |
1/64 |
1/64 |
0.023 |
Hot Finished Square Bar Straightness Tolerance:
HF: 1/8 inch in any 5 foot; but may not exceed 1/8 X (length in ft/5)
| H&T | Hardened and tempered. |
| ANN | Annealed |
| PH | Precipitation hardened. |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| max. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 26.00 | 0.10 max | 19.00 21.00 | 54.7 min | |||
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 0.75 max | 19.00 21.00 | 53.095 min | |||
| SS 310H | 0.04 0.10 | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 19.00 21.00 | 53.885 min | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | 0.08 max | 10.00 14.00 | 2.0 max | 0.045 max | 0.030 max | 16.00 18.00 | 0.75 max | 2.00 3.00 | ||||
| 317 | 0.08 max | 2 max | 1 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 57.845 min | ||||
| SS 317L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 5(C+N) 0.70 max | |||
| SS 321H | 0.04 0.10 | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 4(C+N) 0.70 max | |||
| 347/ 347H | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| max. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| max. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 304H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 306/ 316H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 317 | 7.9 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 347 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000 , MPa 490 | Psi 32000 , MPa 220 | 35 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18‐09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18‐10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 304H | 1.4301 | S30409 | – | – | – | – | – |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 310S | 1.4845 | S31008 | SUS 310S | 310S16 | 20Ch23N18 | – | X8CrNi25-21 |
| SS 310H | – | S31009 | – | – | – | – | – |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 316H | 1.4401 | S31609 | – | – | – | – | – |
| SS 316Ti | 1.4571 | S31635 | SUS 316Ti | 320S31 | 08Ch17N13M2T | Z6CNDT17‐123 | X6CrNiMoTi17-12-2 |
| SS 317 | 1.4449 | S31700 | SUS 317 | – | – | – | – |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 321H | 1.4878 | S32109 | SUS 321H | – | – | – | X12CrNiTi18-9 |
| SS 347 | 1.4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 347H | 1.4961 | S34709 | SUS 347H | – | – | – | X6CrNiNb18-12 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |
Square Bar Weight Formula
0.00788 X ( mm ) Diam X ( mm ) Diam = Weight / Meter
0.00240 X ( mm ) Diam X ( mm ) Diam = Weight / Feet
|
|